Lapox® epoxy adhesives.

Lapox epoxy adhesives for bonding various substrates for household and industrial applications:

1. Marble to marble

2. wood to wood

3. Wood to glass

4. Glass to metal

5. Glass to glass

6. Plastic and rubber.

Packing: 90g, 180g, 450g. 1kg

Lapox Granito Cast is two components modified, epoxy-based system suitable for clear casting application. The system is clear, having excellent optical properties with negligible shrinkage on curing. Faster productivity can be achieved, if curing is performed at higher temperature between 40°C and 60°C. Curing at higher temperature is recommended to achieve optimum performance. 

Applications:

1. Casting of decorative parts 

2. Handicraft items 

3. Paper weights.

4. Table top.

Advantages:

1. Excellent clarity.

2. Good hardness development.

3. Good wetting properties.

4. High gloss finish.

5. Long pot life.

6. Low viscosity.

7. Water and chemical resistant 

Lapox ASR 200 is a two components modified, epoxy-based system suitable for clear casting application. The system is clear, having excellent optical properties with negligible shrinkage on curing. Faster productivity can be achieved, if curing is performed at higher temperature between 40°C and 60°C. Curing at higher temperature is recommended to achieve optimum performance. 

Applications:

1. Casting of decorative parts 

2. Handicraft items 

3. Paper weights.

4. Table top.

Advantages:

1. Excellent clarity.

2. Good hardness development.

3. Good wetting properties.

4. High gloss finish.

5. Long pot life.

6. Low viscosity.

7. Water and chemical resistant 

Lapox Crafto Supreme is two component modified, viscous epoxy adhesive system. When both components are mixed in recommended ratios and cured appropriately at room temperature, an excellent bond strength can be achieved with most of the substrates including glass, metals, plastics, wood, textile and natural stones. Faster productivity can be achieved, if curing is performed at higher temperature between 40°C and 60°C. Curing at higher temperature is recommended to achieve optimum bond strength.

 Applications:

•  Artificial jewelry and jewel stone fixing :

• Bangles 

• Ceramic 

• Handicraft industries 

• Wood and concrete 

Advantages 

• Electrically insulating 

• High bond strength and mechanical strength even in dynamic conditions

• Thermally stable and suitable to perform in extreme conditions 

• Water and chemical resistant 

Mix specifications:

• Mixing ratio (resin: hardener) w/w - 100: 80 

• Mix viscosity at 25°C m Pas ASTM D2196: 25,000 - 30,000 

• Pot life Minutes ASTM D2471: 30 - 45 

• Peak exotherm temperature °C ASTM D2471: Max 70 

• Surface dry - Minutes ASTM D5895: 70 - 90 

• Touch dry - Minutes ASTM D5895: 220 - 240 

• Hard dry -Minutes ASTM D5895: 455 - 475 

Lapox Marbobond Clear is two component modified, epoxy based system suitable for treatment of Italian and other marbles. The system after curing gives an excellent gloss by polishing surface of the marble. The system is room temperature curing, low viscous and has good penetrating properties into cracks for marbles and granites. Faster productivity can be achieved, if curing is performed at higher temperature between 40°C and 60°C. Curing at higher temperature is recommended to achieve optimum performance.

Applications: 

Filling and coating of Italian marbles and granites 

Advantages:

• Good colour stability 

• Good penetrating power into cracks 

• High gloss Low shrinkage 

• System can be pigmented 

• Thermally stable and suitable to perform in extreme conditions 

• Water and chemical resistant 

Mix specifications:

1. Mixing ratio (resin : hardener) w/w - 100 : 30 

2. Mix viscosity at 25°C m Pas ASTM D2196: 500 - 600 

3. Pot life- Minutes ASTM D2471: 80 - 100 

4. Peak exotherm temperature °C : Max 60 

5. Surface dry - Minutes ASTM D5895: 220 - 260 

6. Touch dry Minutes ASTM D5895: 360 - 400 

Lapox® Duratite is two component modified, thixotropic epoxy adhesive system. When both components are mixed in recommended ratios and cured appropriately at room temperature, an excellent bond strength can be achieved with most of the substrates including glass, metals, reactive plastics, wood, textile and natural stones. Faster productivity can be achieved, if curing is performed at higher temperature between 40°C and 60°C. Curing at higher temperature is recommended to achieve optimum bond strength.

 Applications:

1. Artificial jewelry and jewel stone fixing.

2. Wood furniture industries.

3. Marble joint.

4. Concrete.

5. Glass and metal.

6. Sports goods.

7. Automobile components and general engineering components.

8. Handicrafts.

Advantages 

1. Long working time.

2. High bond strength and mechanical strength even in dynamic conditions 

3. Thermally stable and suitable to perform in extreme conditions.

4.  Water and chemical resistant

Lapox® Powergrip is two components modified, viscous epoxy adhesive system. When both components are mixed in recommended ratios and cured appropriately at room temperature, an excellent bond strength can be achieved with most of the substrates including glass, metals, reactive plastics, wood, textile and natural stones. Faster productivity can be achieved, if curing is performed at higher temperature between 40°C and 60°C. Curing at higher temperature is recommended to achieve optimum bond strength. 

Applications:

1. Artificial jewellery and jewel stone fixing.

2. Electrical components.

3. General engineering components.

4. Natural stones Souvenirs and handicrafts.

5. Sports goods 

Advantages:

1. High bond strength.

2. High mechanical strength even in dynamic conditions.

3. Long pot life.

4. Thermally stable and suitable to perform in extreme conditions.

5.  Water and chemical resistant

Lapox® Ultra is two component modified, viscous epoxy adhesive system. When both components are mixed in recommended ratios and cured appropriately at room temperature, an excellent bond strength can be achieved with most of the substrates including glass, metals, laminates, wood, textile and natural stones. Faster productivity can be achieved, if curing is performed at higher temperature between 40°C and 60°C. Curing at higher temperature is recommended to achieve optimum bond strength.

 Applications:

1. Artificial jewellery and jewel stone fixing.

2. Automobile components.

3. Ceramic works.

4. Construction.

5. Electrical components.

6. General engineering components.

7. Souvenirs and handicrafts.

8. Sports goods.

Advantages:

1. Adequate pot life.

2. Excellent electrical insulation properties.

3. High bond strength.

4. High mechanical strength even in dynamic conditions.

5. Thermally stable and suitable to perform in extreme conditions.

6. Water and chemical resistant.